Code Description D(H8) d(h9) B(-0/+0.2) r n

752

K752 is a two piece double-acting sealing set which consists of one special mixture PTFE prole ring and an o-ring as energizing element.

PRODUCT ADVANTAGES
• Able to use at high pressures and low peripheral speeds
• Low friction , free of stick-slip
• Simple groove design and low axial housing heights
• Long service life
• High sliding speed
• Wide range of temperature and chemicals depending on the o-ring material
• Minimum static and dynamic friction coeficient for a minimum energy loss and operating temperature

APPLICATION
Mobile hydraulics , grippers and rotary joints.  

INSTALLATION
We recommend using special assembly tool (See section; Hydraulic Sealing Elements General Installation Information). It is very important that the assembly tools must be of soft material and have no sharp edges. Before installation the sealing element must be oiled with system oil.

 

MATERIAL   CODE
NBR 70 SHORE A NB7001
PTFE /BRONZE   PT6003

OPERATING CONDITIONS

MEDIA

Mineral Oils
(DIN 51524)

HFA and
HFB

HFC

TEMPERATURE

-30°C
+105°C

+5°C
+60°C

-30°C
+60°C

PRESSURE

≤300 bar

≤300 bar

≤300 bar

SPEED

≤5.0 m/s

≤0.5 m/s

≤5.0 m/s

PERIPHERAL SPEED ≤5.0 m/sn ≤5.0 m/sn ≤5.0 m/sn

Note: The above data are maximum values and cannot be used at the same time.

SURFACE ROUGHNESS

Ra

Rmax

Sliding Surface Ød

≤0.2 μm

≤2.0 μm

Groove Base ØD

≤1.6 μm

≤6.3 μm

Groove Flanks B

≤3.2 μm

≤16 μm

Note: It is recommended to have 50% to 90% of the working surface material contact area value.

PERMISSIBLE SEALING GAP

B (mm)

S max (mm)

x

100 bar

200 bar

300 bar

2.2

0.15

0.10

0.075

3.2

0.20

0.15

0.10

4.2

0.20 0.15 0.10

6.3

0.30

0.20

0.15

8.1

0.30

0.20

0.15

Note: The largest sealing gap value occurring on the non-pressurized side of the seal does have a vital importance for the function of the seal and in this respect it is quite important to use the S value lower than the above indicated numbers.  

 

NOTES
For special applications that require high temperatures or resistance to chemicals , rod seal is being manufactured with special mixture PTFE and FKM material.